High Impact Plastic Alloy ABS PE Sheet for Luggage and Hat Forming

• Customization: Available
• After-sales Service: Online Technical Support
• Warranty: 12 Months
• Model NO.: AP6589
• Material: ABS
• Kind: Hard Plastic Sheet
• Water Absorption: ＜0.01%
• Contraction Percentage: 0.4%~1.4%
• Tensile Strength: 3.9MPa
• Color: Customized
• Density: 0.95
• Size: Customized
• Samples: Free to Buyers
• Transport Package: Pallet or Wooden Case
• Specification: customized
• Trademark: Yingli
• Origin: Hebei
• HS Code: 3926901000
• Production Capacity: 100t/Year

Product Description

                        Product Description
High Impact Plastic Alloy ABS PE Sheet for Luggage and hat Forming

ABS sheet is an emerging material in the plastic sheet industry, it is is a terpolymer of butadiene and styreneits, its full name is Acrylonitrile-butdiene-styrene. ABS is the most widely used polymer, it organically unifies the various properties of PB, PAN and PS, and has excellent mechanical properties of toughness, rigidity and stiffness in balance.

Features
1) Low density, easy welding and processing, with superior chemical resistance, heat resistance and impact resistance, non-toxic,smelless.
2) The main colors are black white, computer color, other colors can also be customized according to customer requirements.
3) PP extruded sheet has the characteristics of light weight, uniform thickness, smooth surface, good heat resistance, high mechanical strength, excellent chemical stability,        electrical insulation and non-toxic.

 

Polypropylene (PP) Extrusion board is a kind of plastic sheet made by extrusion, calendering, cooling and cutting by adding various functional additives into PP resin. 

Plastic Material ABS, HIPS, HDPE, LDPE, PP, ASA, TPO, ABS/PC. ABS, ABS/ASA etc
Color Customized as your samples or pantone color numbers
Surface type Gloosy, smooth, matte, sand, pvc wood film, existing textures or customized textures
Application Thermorforming Thickness 0.7-14mm

GENERAL TECHNICAL DATA
Typical Properties	Method/Unit	Test Result
Density(SG)	SO 1183 (g/cm3)	1.2
MVR	ISO1133(ml/10min)	18
Tensile Strength at Yield	ISO 527(Mpa)	40
Tensile Elomgation	ISO527(%)	30
Flexural Strength	ISO178(Mpa)	76
Flexural Modulus	ISO178(GPa)	2.2
Izod Impact @23 Deg C	ISO 180(KJ/m^2)	30
Izod Impact @-30 Deg C	ISO 180(KJ/m^2)	15
harpy Impact@23 Deg C	ISO 179(KJ/m^2)	15
harpy Impact@230 Deg C	ISO 179(KJ/m^2)	8
Vicat Softening  50ºC/hr;1KG	ISO306(ºC)	104
Temperature   50ºC/hr;5KG	ISO306(ºC)	100
Hardness(ball indentation)	ISO 2039(Mpa)	85
Heat Deflection 1.8MPa,unanneaied	ISO75/A(ºC)	83
Temperature   1.8MPa,anneaied	ISO75/A(ºC)	100
Vicat Softening(50N)	ISO 306(deg C)	99
Fire Rating	UL94	HB
Tolerances -Length	mm	+/- 2
Tolerances -Width	mm	+/- 2
Tolerances  -Thickness	mm	+/- 2